ASTM B575 Hastelloy C-4 nickel strip,UNS N06455nickel plate price, Hastelloy C-4 nickel bar

Short Description:

Hastelloy C-4 is a Nickel-Chromium-Molybdenum alloy that offers exceptional stabilization at the elevated temperatures, good ductility and resistance to corrosion properties. It retains its characteristics even after aging up to 1200oF to 1900oF or 649oC to 1038oC. Alloy C-4 offers resistance to grain development precipitation in the welding area so it is highly suitable for the chemical processes in the welding condition. It offers extremely high resistance to stress corrosion cracking and oxidizing conditions up to 1900oF or 1038oC. Hastelloy C-4 offers resistance to mineral acids, organic and inorganic acids, sea water and brine solutions. It has service temperature up to 1900oF or 1038oC. Outstanding resistance to high temperature corrosion and stress corrosion cracking. Great material for use in chemical processing plants and nuclear fuel processing.

Send email to us

Product Detail

Product Tags

Other Designations

▪ ASTM B574
▪ ASTM B575
▪ ASTM B619
▪ ASTM B622
▪ ASTM B626
▪ DIN 2.4610

Chemical Composition

The chemical composition of Hastelloy C-4 is outlined in the following table.

Element	Content (%)
Chromium, Cr	14-18
Molybdenum, Mo	14-17
Iron, Fe	3 max
Cobalt, Co	2 max
Manganese, Mn	1 max
Titanium, Ti	0.7 max
Silicon, Si	0.08 max
Phosphorus, P	0.04 max

Mechanical Properties

The mechanical properties of Hastelloy C-4 are outlined in the following table.

Properties	Metric	Imperial
Tensile strength	738 MPa	107000 psi
Yield strength ( @ 0.2% offset)	492 MPa	71400 psi
Elastic modulus	211 GPa	30600 ksi
Elongation at break (in 50.8 mm)	42%	42%

Machinability

Hastelloy C-4 can be machined using conventional methods.

Forming

Hastelloy C-4 can be easily formed using conventional techniques.

Welding

Except submerged arc and oxy-acetylene welding methods, Hastelloy (r ) C-4 can be welded using all other welding methods.

Heat Treatment

Hastelloy C-4 is heat treated by annealing at 1066°C (1950°F) followed by quenching.

Forging

Hastelloy C-4 is hot forged at 955 to 1177°C (1750 to 2150°F).

Hot Working

Hastelloy C-4 is hot extruded or hot worked similar to that of stainless steels.

Cold Working

Hastelloy C-4 can be cold worked using conventional methods.

Annealing

Hastelloy C-4 is annealed at 1066°C (1950°F) followed by quenching.

Aging

Hastelloy C-4 is aged at 649°C (1200°F) for 10 h in order to improve its yield strength and ductility without decreasing its ultimate tensile strength.

Hardening

Hastelloy C-4 is hardened by cold working.

Applications

▪ Chemical processing equipment
▪ Nuclear fuel processing

available sizes and specifications

Hastelloy C-4 available sizes and specifications
Grade	Hastelloy C-4
Nickel plate	Thickness: 0.3mm - 150.0mm Width: 1000mm - 3000mm
Nickel strip/ nickel foil	Thickness: 0.02mm - 16.0mm Width: 5mm - 3000mm
Nickel coil	Thickness: 0.3mm - 16.0mm Width: 1000mm - 3000mm
Nickel pipe	Outside diameter: 6mm - 1219mm Thickness: 0.5mm - 100mm
Nickel Capillary Pipe	Outside diameter: 0.5mm - 6.0mm Thickness: 0.05mm - 2.0mm
Nickel bar	Diameter: Ф4mm - Ф600mm
Nickel wire rod	Diameter：Ф0.01mm - Ф6mm